Wire Cable PVC Compound 70 Degree 90 Degree

Model NO.: 70 degree 90 degree
Trademark: longtai
Specification: 70-----110degree
Origin: China
HS Code: 3904210000
Model NO.: 70 degree 90 degree
Trademark: longtai
Specification: 70-----110degree
Origin: China
HS Code: 3904210000
1.Technical specifications of 70 ºC pvc compound
 
Tensile strength MPa 20.5
Fracture tensile strain % 320
Ageing temperature ºC 100
Ageing time h 168
Tensile strength after ageing MPa 22.5
Max change of tensile strength % +12
After ageing fracture tensile strain % 290
Max change of fracture tensile strain % -10
Thermal deformation % 28
Thermal ageing quality loss g/m2 19
200ºC thermal stability time min 90
20ºC volume resistivity  Ω.cm 2.0*1011
 
 
 
Technical specifications of  90 ºC pvc resin compound
 
Tensile strength MPa 20
Fracture tensile strain % 330
Ageing temperature ºC 100
Ageing time h 240
Tensile strength after ageing MPa 21.5
Max change of tensile strength % +8
After ageing fracture tensile strain % 310
Max change of fracture tensile strain % -6
Thermal deformation % 28
Thermal ageing quality loss g/m2 9
200ºC thermal stability time min 120
20ºC volume resistivity  Ω.cm 2.0*1010
 
2,Use and standard: wire and cable
 
3,Process: extrusion
 
4,Appearance: cylindrical particles,  plastication should be good, the color and luster is even, without obvious impurity.
 
5,color: Any colors, base on requirement.
 
6,Packing: 25kg net weight per in a kraft bag.
 
7, Transportation and storage:
This kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.
 
We will also produce the products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting  compounds, Heat-resistant compounds, and low smoke low halogen compounds, Transparent PVC compounds etc.
  1.Technical specifications of 70 ºC pvc compound
 
Tensile strength MPa 20.5
Fracture tensile strain % 320
Ageing temperature ºC 100
Ageing time h 168
Tensile strength after ageing MPa 22.5
Max change of tensile strength % +12
After ageing fracture tensile strain % 290
Max change of fracture tensile strain % -10
Thermal deformation % 28
Thermal ageing quality loss g/m2 19
200ºC thermal stability time min 90
20ºC volume resistivity  Ω.cm 2.0*1011
 
 
 
Technical specifications of  90 ºC pvc resin compound
 
Tensile strength MPa 20
Fracture tensile strain % 330
Ageing temperature ºC 100
Ageing time h 240
Tensile strength after ageing MPa 21.5
Max change of tensile strength % +8
After ageing fracture tensile strain % 310
Max change of fracture tensile strain % -6
Thermal deformation % 28
Thermal ageing quality loss g/m2 9
200ºC thermal stability time min 120
20ºC volume resistivity  Ω.cm 2.0*1010
 
2,Use and standard: wire and cable
 
3,Process: extrusion
 
4,Appearance: cylindrical particles,  plastication should be good, the color and luster is even, without obvious impurity.
 
5,color: Any colors, base on requirement.
 
6,Packing: 25kg net weight per in a kraft bag.
 
7, Transportation and storage:
This kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.
 
We will also produce the products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting  compounds, Heat-resistant compounds, and low smoke low halogen compounds, Transparent PVC compounds etc.
 

PC Stand

PC Stand

PC strand is mainly used for the reinforcement of prestressed concrete structures, such as large-span railway and road bridges, major bridges, silos, buildings, dams, floor slabs, foundations, large concrete vessels, atomic reactor buildings, stadiums, airport hangers, pre-cast segments, crane beams, anchorages and multi-story industrial buildings etc.
Our PC strand is also used for the construction of highways, poles and water towers in civil construction, and energy source sea transportation, house buildings, water control projects, and rock and earth anchoring components to increase the tensile force.

Pc Stand,High Carbon Pc Stand,Unbonded Pc Stand,Computer Stand

HENGSHUI YUZHENG IMPORT AND EXPORT CO., LTD. , https://www.ironnailwiremesh.com